No.169,Prof Xingbo Liu,10月26日报告

 
报告题目Ni-Base Superalloys for Advanced Ultra-supercritical Power Plants
报告人:Prof. Xingbo Liu.
报告时间:2015年10月26日下午3:30
报告地点:材料A楼308号
邀请人:张德良
报告人简介
Dr. Xingbo Liu graduated from University of Science and Technology Beijing in
1999, and he subsequently went to West Virginia University as a postdoc. Currently, he is the professor & Associate Chair for Research in Mechanical & Aerospace Engineering Department at WVU. Dr, Liu’s main research interests are advanced high temperature materials for next generation energy conversion and storage and his research focuses are Ni-base superalloys and solid oxide fuel cells. Dr. Liu has received numerous awards including R&D 100 Award (2011), TMS Early Career Faculty Fellow Award (2010), WVU CEMR Researcher of the Year (2011, 2015) and Outstanding Researcher Awards (2011, 2009, 2008), as well as many others. Recently, Dr. Liu was elected as the Fellow of ASM International (2015)
 
报告简介
The development of next generation Advanced Ultra-supercritical (A-USC) Coal-fired Power plants provide several grant challenges on Ni-base superalloys in terms of mechanical properties, microstructural stabilities, processing, and corrosion resistance and monitoring. Inconel 740 has gained much attention recently as a candidate material for use as tubing in USC power plant applications, but its microstructural stability at USC temperatures has been shown to be an issue through observations of gamma prime coagulation, transformation of gamma prime to eta phase, and also through the formation of G phase. We evaluate the effect of nominal Al content on the microstructural stability of wrought IN 740 at A-USC temperatures for times up to 2000 hours. We also provide a comparison of the microstructural stability of both wrought and cast versions of IN 740 evaluated under these conditions. Freckle is a primary defect formed during the remelting of superalloy ingots. We have developed an improved freckle criterion that preserves the anisotropic nature of the permeability tensor throughout the derivation and provides improved resolution on freckle prediction. A clear separation between the freckled and non-freckled experiments was obtained for all compositions. The effect of the tilted solidification front over the freckling potential was corroborated, and the results suggested that the directionality of permeability affects the location within the mush layer of the potential nucleation sites for the channels leading to freckles. The final part of this presentation will be devoted to our current work on developing in-situ monitoring of coal-ash corrosion of Ni-base superalloys as A-USC boiler tubes, which is based on our patented technology.
返回
版权所有©上海交通大学材料科学与工程学院 通讯地址:上海市东川路800号 联系电话:34203098 邮编:200240