Precipitation process in a Mg–Gd–Y alloy grain-refined by Al addition

 

论文名称

Precipitation process in a Mg–Gd–Y alloy grain-refined by Al addition

发表期刊名称

Materials Characterization

简介

The precipitation process in Mg–10Gd–3Y (wt.%) alloy grain-refined by 0.8 wt.% Al addition has been investigated by transmission electron microscopy. The alloy was given a solution treatment at 520 °C for 6 h plus 550 °C for 7 h before ageing at 250 °C. Plate-shaped intermetallic particles with the 18R-type long-period stacking ordered structure were observed in the solution-treated state. Upon isothermal ageing at 250 °C, the following precipitation sequence was identified for the α-Mg supersaturated solution: β″ (D019) → β′ (bco) → β1 (fcc) → β (fcc). The observed precipitation process and age hardening response in the Al grain-refined Mg10Gd3Y alloy are compared with those reported in the Zr grain-refined counterpart.

图片

发表时间

2014.02

影响因子

1.845

完成人

Jichun Dai, Suming Zhu, Mark A. Easton, Wenfan Xu, Guohua Wu, Wenjiang Ding

联系人

吴国华

电话

13671800698

返回
版权所有©上海交通大学材料科学与工程学院 通讯地址:上海市东川路800号 联系电话:34203098 邮编:200240