Effects of processing parameters and Ca content on microstructure and mechanical propertie

 

论文名称

Effects of processing parameters and Ca content on microstructure and mechanical properties of squeeze casting AZ91-Ca alloys

发表期刊名称

Materials Science and Engineering A

简介

AZ91–(1–3 wt%) Ca alloys were prepared by direct squeeze casting, in which the melt was solidified under applied pressure. The effects of processing parameters (such as applied pressure and pouring temperature) and Ca content on microstructure and mechanical properties of squeeze casting AZ91–Ca alloys were investigated. The results indicate that the microstructure was refined with the increase of applied pressure, and the mechanical properties were improved. When the pouring temperature was lowered down to near the liquidus, the microstructure was further refined and α-Mg grains turned rosette-like. The negative effect on ambient temperature mechanical properties caused by the addition of Ca into AZ91 alloy was inhibited by squeeze casting. Compared to conventional casting, squeeze casting process can offer AZ91–Ca alloys better mechanical properties, especially in elongation to failure (Ef).

图片

发表时间

2014.02

影响因子

2.567

完成人

Yang Zhang, Guohua Wu*, Wencai Liu, Liang Zhang, Song Pang, Yingdong Wang, Wenjiang Ding

联系人

吴国华

电话

13671800698

返回
版权所有©上海交通大学材料科学与工程学院 通讯地址:上海市东川路800号 联系电话:34203098 邮编:200240