Effect of chemical composition on the microstructure, tensile properties and fatigue behav

 

论文名称

Effect of chemical composition on the microstructure, tensile properties and fatigue behavior of sand-cast Mg–Gd–Y–Zr alloy

发表期刊名称

Materials Science and Engineering A

简介

Microstructures, tensile properties and high cycle fatigue behavior of sand-cast Mg–Gd–Y–Zr alloys with different Gd and Zr contents have been investigated. With decreasing Gd content from 9 to 11 wt%, the amount of eutectic phase in sand-cast Mg–xGd–3Y–0.5Zr alloys and of the β′ precipitates in peak-aged (T6) conditions decreased, and increasing Zr content from 0.3 to 0.5 wt% led to a decrease in the grain size. The variation of Gd content had a slight influence on the tensile properties, while Zr content had an obvious influence on the tensile properties particularly the elongation. Gd and Zr affected the fatigue behavior in different ways, i.e. the increase of Zr content improved the fatigue strength while the increase of Gd content extends the fatigue life under relatively high stress.

图片

发表时间

2014.08

影响因子

2.567

完成人

Longkang Jiang, Wencai Liu*, Guohua Wu, Wenjiang Ding

联系人

刘文才

电话

15921573539

返回
版权所有©上海交通大学材料科学与工程学院 通讯地址:上海市东川路800号 联系电话:34203098 邮编:200240